Effects of parameters on microstructure of bonding interface formed by overlapping laser cladding
In order to improve the cladding quality and to control the bonding interface of the layer formed by overlapping laser cladding
the effects of parameters on the microstructure of bonding interface were studied. The results show that when scanning speed
powder feeding rate and laser power change in the range of 100-250 mm/min
6-7.5 g/min and 1 500-2 500 W
respectively
the bonding region does not appear a white layer and presents different morphologies. One of morphologies is the continuous epitaxial growth with inherited microstructures and directions
and the other is discontinuous epitaxial growth. This is related to the effects of parameters on the depth of remelting region of a shifted dendrite
the orientation and molten degree of grain of a prior layer surface
and the con- vection in the molten pool.
关键词
Keywords
references
GU D D, SHEN Y F, LU Z J. Microstructural characteristics and formation mechanism of direct laser-sintered Cu-based alloys reinforced with Ni particles [J]. Materials and Design, 2009,30:2099-2107.[2] SMUROV I. Laser cladding and laser assisted direct manufacturing [J]. Surface & Coatings Technology, 2008,202:4496-4502.[3] ZHANG F Y, CHEN J, TAN H,et al.. Composition control for laser solid forming from blended elemental powders [J]. Optic. Laser. Technol., 2009,41:601-607.[4] YANG N. Concentration model based on movement model of powder flow in coaxial laser cladding [J]. Optic. Laser. Technol., 2009,41:94-98.[5] 刘要武. 铜基材料上激光熔覆镍基合金的结合强度[J]. 光学 精密工程,1997,5(1):62-66. LIU Y W. Binding strength between coating layer and the substrate cladded Ni-base alloy on the copper alloy by laser [J]. Opt. Precision Eng., 1997,5(1):62-66. (in Chinese)[6] POPRAWE R. 激光制造工艺[M]. 北京: 清华大学出版社, 2008:149-153. POPRAWE R.Laser Manufacture Technics[M]. Beijing: Tsinghua University Press, 2008:149-153. (in Chinese)[7] 刘要武. H62黄铜基材间显微组织及微区分析[J]. 光学 精密工程,2000,8(1):26-28. LIU Y W. Analysis of microstructure between Ni-Cr-B-Si laser cladding layers and H62 brass bases [J]. Opt. Precision Eng., 2000,8(1):26-28. (in Chinese)[8] 钟敏霖, 刘文今. 国际激光材料加工研究的主导领域与热点[J]. 中国激光,2008,35(11):1653-1659. ZHONG M L, LIU W J. Leading areas and hot topics on global laser materials processing research [J]. Chinese Journal of Lasers, 2008,35(11):1653-1659. (in Chinese)[9] 张庆茂, 刘喜明, 关振中,等. 送粉式宽带激光熔覆搭接基础理论的研究[J]. 金属热处理,2001(2):25-28. ZHANG Q M, LIU X M, GUANG Z Z, et al.. Fundamental investigation on overlapping coating formed by broad-beam powder feeding cladding [J]. Heat Treatment of Metals, 2001(2):25-28. (in Chinese)[10] 刘喜明. 送粉式激光熔覆基础理论研究 . 长春: 中国科学院长春光学精密机械研究所,1998:87-89. LIU X M.An Investigation on the fundamentals of powder feeding type laser cladding . Changchun: Changchun Institute of Optics, Fine Mechanics and Physics,Chinese Academy of Sciences,1998:87-89. (in Chinese)[11] 李言祥, 吴爱萍. 材料加工原理 [M]. 北京: 清华大学出版社, 2006:132-136. LI Y X,WU A P. Principle of Materials Processing[M]. Beijing: Tsinghua University Press,2006:132-136. (in Chinese)[12] 黄卫东, 林鑫, 陈静,等. 激光立体成形 [M]. 西安: 西北工业大学出版社, 2007:50-70. HUANG W D, LIN X, CHEN J, et al.. Laser Three-dimensional Forming [M]. Xian: Northwestern Polytechnical University Press, 2007:50-70. (in Chinese)